Enamelled Aluminium winding wire

1. Conductor resistance ¡ª The resistance of a conductor is proportional to its length and inversely proportional to its cross-sectional area.
2. Conductivity¡ªBased on the resistance 1/58ohm (0.017241 ohm) of a standard soft copper wire with a length of 1m and a cross-sectional area of 1mm2 at 20¡æ, it is called 100% conductivity. The greater the resistance, the lower the conductivity, and the two are inversely proportional.
3. Bending resistance¡ªfix one end of the single wire, add weight to the other end to make it vertically downward, and then bend it back and forth 180 times until the wire breaks. The more bending times, the stronger the bending resistance.
4. Tensile breaking force¡ªthe maximum load weight or force applied to the specimen to break it during a tensile test.
5. Tensile strength¡ªthe breaking force per unit area to bear when the sample is broken during the tensile test.
6. Elongation ¡ª the ratio of the length of the sample after being stretched until it breaks to the original length at the specified standard distance. Conductors have different impedances at different temperatures.
Generally, 20¡ãC or 25¡ãC is the standard. The higher the temperature, the greater the impedance.

Water quality affects the production of lacquer wires?

The production water production water in the lacquered wire has a variety of uses, and like, the requirements for water quality are also different. Depending on the purpose of use, the water quality can be divided into: annealing furnace water seal water, equipment cooling water, lubricant manufacturing water, etc.

Enameled wire is a main type of winding wire. It is made of a metal conductor as a conductive inner core and coated with a polymer insulating layer. It is mainly composed of these two parts; it is the conversion of electromagnetic energy into mechanical energy, heat energy, sound energy, light energy or machinery Functional materials that convert energies such as heat, heat, chemistry, sound and light into electromagnetic energy.

Aromatic polyimide enameled wire has good heat resistance, softening breakdown resistance, radiation resistance, severe cold resistance and chemical resistance. Among them, many test indicators such as unidirectional scratching, breakdown voltage, and thermal softening are far Far better than ordinary enameled wire.

Type of magnetic wire is divided into enameled wire, wrapping wire, insulated wire, combined wires and others,Mainly used in motors, electrical appliances, instruments, transformers, etc., to generate electromagnetic effects by winding coils, and use the principle of electromagnetic induction to achieve the purpose of converting electrical energy to magnetic energy

Aluminum bare magnet wire (Anodized Bare Aluminium wire) belongs to the special electromagnetic wire and the insulation layer is the aluminum oxide .Because of no thermal aging phenomenon, it can be used as insulation level of class 220.
The insulation layer of such product is thin, high temperature resistance and insulation performance stability,which is the best choice for low voltage winding wires with producing high temperature, poor environment, heat dissipation difficulty and so on. It can widely be used in electromagnetic industries at home and abroad.

Features of Aluminum Enameled Electric Wire 1.5mm For Moxico
1) Excellent bending performance
2) High flexibility of enamel
3) Good wear resistance
4) High mechanical properties
5) Higher thermal performance
6) Good resistance to refrigerants and Freon
7) Suitable for windings subjected to continuous high temperature and mechanical stress
8) Good chemical resistance
9) Excellent mechanical and chemical properties

A brief introduction to the advantages and disadvantages of copper wire and aluminum wire:Same area:

1, copper wireis large load than aluminum wire . 2, copper wire is more flexible than aluminum wire. 3 copper wire is lower resistivity than aluminum wire. 4,copper wire is more stable than aluminum wire. 5, however, copper wirer price is 3.5 times higher than aluminum wire.

The enameled wire manufacturer takes you to understand the high-temperature paint wrap of high-temperature paint wires, and it is necessary to judge, whether its appearance, size, and performance meet the technical standards of the product and user technical agreements. After the measurement, test, the technical standards of the product and the technical agreement of the product are compared to the requirements for qualified products, which does not meet the requirements for unqualified products.

Heat resistance refers to the properties of a substance that can maintain its excellent physical and mechanical properties under heated conditions. The highest use temperature of commonly used materials to characterize. There are different standards and test methods for different materials. Such as plastics are generally expressed by Martin heat-resistant temperature. The coating industry uses a blast constant temperature oven or a high temperature furnace. After it reaches the specified temperature and time, the surface condition of the paint film is inspected, tested, or other properties such as impact, bending, water immersion, salt spray test, etc., and then before and after Test data representation. All coatings used in higher temperature occasions must use heat resistance as an important technical indicator of the coating film

The enamel wire is a major variety of winding wires, composed of two conductors and insulating layers, after the naked wire is deck, and then painted, baked.However, it is not easy to produce products that meet the standard requirements, but also meet customer requirements, it is affected by factors such as raw materials, process parameters, production equipment, environment, and therefore, the quality characteristics of various enameled wires are different, but they haveFour major properties of mechanical properties, chemical properties, electrical properties, and thermal performance.

The samples for the dielectric strength test are also twisted pairs, and the number is 5 pairs. During the test, the voltage was applied at a boosting rate of 500V/S until breakdown, and the voltage at the time of breakdown was recorded. The requirements for dielectric strength in the NEMA MW1000 standard will vary according to different wire diameters, different paint film thicknesses, and different enameled wire types.

Enameled wire is a type of electromagnetic wire, usually refers to the insulation wire used to make coil or winding in electrical products. It is also called the winding wire.
The electromagnetic wire must meet the requirements of various applications and manufacturing processes. The former includes its shape, specification, working at high temperature in short and long time, as well as the strong vibration and centrifugal force under high speed on certain occasions, resistance to corona and breakdown under high voltage, and chemical corrosion resistance in special atmospheres, and the requirements for tensile, bending and wear, as well as the requirements of drawing, bending and wear during winding and inlaying. Swelling and erosion during immersion and drying.

Copper-clad aluminum wire is made of a solid aluminum core covered with a copper skin in order to improve its performance in the field. Copper clad aluminum wire is very different from solid EC grade aluminum wire. For one, CCA belongs to a species of metals known as ¡°Bimetallics,¡±
Conductor materials: copper and aluminum

3.1 Elongation:
The standard refers to GB/T6109, inspection method: stretch the instrument
Calculation method: ratio of (length after stretching-length before stretching)/length before stretching;

3.2 Snap off:
The standard is to pull at a speed of 2 meters per second to check that the paint film is not cracked,

3.3 Round rod winding:
Wrap the enameled wires of different specifications and the corresponding copper rods around ten times to check that the paint film is not cracked. The diameter of the copper rods refers to the requirements of GB/T6109;

3.4 Thermal shock: Put the winding enameled wire in an oven (hanging in the middle of the oven) for 0.5 hours. The temperature of the oven corresponds to the specification requirements of the enameled wire. Refer to GB/T6109. After the drying, check that the paint film is not cracked.

Enameled wire is used for camcorder, electronic clock, micro relay, automobile, electronic instrument, washing machine, TV element, etc. Development direction in the diameter, use the specification range of ¦Õ0.06 ~ 0.08 mm and all thickened insulation

The temperature resistance of composite enameled wire can reach above 520 degrees.
Composite enameled wire is an ideal wrapping wire for large-scale low-voltage and high-current electrical appliances such as power oil-immersed, dry-type, special transformers, electric welding machines, reactor rectifiers, electromagnetic separators, etc., with excellent electrical performance and stability.

What is called Magnet Wire? The magnetic wire is a copper wire with an enamel (a kind of paint ) coating on it, and used for transformer coils and motor coils. Copper wire is a conductor, like bare copper.

Standards Of Enameled Wire includes
1）IEC 60317 for Europe
2）JIS C3202 for Asia
3）NEMA MW 1000C (inch) or NEMA MW 1000C metric (mm) for North America

The selection criterion of the electromagnetic wire is not considered for resistance, as the problem of resistance and fever can be done by selecting the same cross-sectional wire, it is the main consideration of the thick wire or the thin wire is mainly considered Operability.

Enameled wire motors, electrical appliances, home appliances, communications, electronic information, instrumentation, power tools, automobiles and other industries provide supporting basic material industries. They are the main and key raw materials for electromagnetic windings of motors and electronic instruments. The rapid development of electronic products, etc., has brought a broader application field and market to enameled wires, but at the same time, higher requirements have been put forward for enameled wires, and enameled wires have continued to develop towards a high level and high quality.

Round Enameled Wire type: Aluminum Wire and Copper Wire
Application:used for transformers, inductors, motors, generators, dry type transformer, Cast Resin Transformers
Dimension: Aluminum : 0.2-9.2mm; Copper: 0.016-7mm

UL Certificated 220 High Thermal Class Oxidized Film Aluminum Wire and aluminum strip insulated with aluminum oxide film are used in the fields of electronics, missiles, nuclear reactors, aerospace and aircraft industries. The oxide film has high flexibility and is suitable for winding electromagnetic coils of various shapes and sizes. The use of round or rectangular aluminum wires and aluminum strips can save 50% of metal, so it has commercial value. For example, linear motors and medical equipment industries are widely used because of their light weight and low inertia. For rotating equipment, light weight can simplify the dynamic balance, thus reducing the vibration generated by the dynamic balance, thereby improving the sensitivity of the moving coil and its high-frequency response.

To weld the lead aluminum enameled wire, it is necessary to remove the paint (there are very few household electric fans with very low requirements, and the ballast manufacturer does not remove the paint). The paint removal methods are listed below.
(1) It can be scraped with a blade,
(2) It can be peeled with a centrifugal knife,
(3) The paint can also be rubbed off with a grinding wheel,
(4) Of course paint remover is also available,
(5) You can also use high-temperature tin to burn the paint,
(6) Some people burn with fire
(7) Of course you can also use paint remover to remove paint

The paint is a process of painting the paint of the enameled wire to form a uniform lacquer layer of a thickness on the metal conductor. This is related to several physical phenomena and painting methods of liquid.

The wire drawing metal processing technology can form fine lines on the surface of the metal material, which makes the metal more textured, and is used as a decoration by users and is well-loved. In the production process, the drawing lubricating fluid is indispensable in the drawing metal processing technology. It is widely used in the lubrication of the middle drawing, small drawing and micro drawing of enameled copper wire. So how to choose this kind of drawing fluid?

Nomex covering corresponds to class H insulation is mainly used in the construction of condensers and capacitors. Main application of it is in shielding of cables in high temp. environments (200¡ãC) such as dry type transformers, military and aerospace cables. Nomex covered conductors are more effective in condition where temperature resistance and dielectric strength requirements are high.
Application of Nomex Paper Covered Aluminum wire :
Mobile Transformer,Traction Transfomers,Pole-mounted distribution transformers,Power substantions,rectifiers,oil-immersed transfomer coil winding.

ENAMELED ROUND ALUMINUM WINDING WIRES are widely used for Oil-immersed transformer windings, Dry-type transformer, High temperature transformer, Motor, transformer, generator, welding machine; Sealed motor, Power tools motor, Auto alternators motor, Magnet coil, High power motor, household electro motors and micro-motors;

The coating is a process of forming a uniform coating layer of a coating wire to form a uniform coating layer on a metal conductor. This is related to some physical phenomena and painting methods of liquid.

In the long-term thermal aging test, three or more temperature points are usually selected for accelerated aging, commonly known as “three-point aging”.

The samples for the aging test are stranded enameled wire pairs. The production of the stranded pairs should meet the requirements of ASTM D2307 or NEMA 1000 standards, including the weight to be applied when making the stranded pairs, the number of twisted turns, the effective length of the stranded area, and The length of the two ends of the twisted pair, etc. When making a twisted pair, the required force and the number of twist turns will vary depending on the diameter of the wire. The effective length of the stranded area has nothing to do with the wire diameter, the effective length is 121¡À6 mm, and the two ends are at least 50 mm long. At least 10 twisted pairs per temperature point and mounted on twisted pair racks for high temperature aging test.