What is meant by winding wire?

Water quality affects the production of lacquer wires?

The production water production water in the lacquered wire has a variety of uses, and like, the requirements for water quality are also different. Depending on the purpose of use, the water quality can be divided into: annealing furnace water seal water, equipment cooling water, lubricant manufacturing water, etc.

1. Mechanical function: including elongation, return angle, softness and adhesion, scraping, tensile strength and other items.
2. Heat resistance: including thermal shock and softening breakdown test.
3. Electricity includes: breakdown voltage, lacquer film continuity and DC resistance test.
4. Chemical resistance includes solvent resistance and welding.

The enameled wire manufacturer takes you to understand the high-temperature paint wrap of high-temperature paint wires, and it is necessary to judge, whether its appearance, size, and performance meet the technical standards of the product and user technical agreements. After the measurement, test, the technical standards of the product and the technical agreement of the product are compared to the requirements for qualified products, which does not meet the requirements for unqualified products.

Enameled Aluminum Wire Compared To Enameled Copper Wire have some advantages
Aluminum /Copper Wire/foils
Dimension:0.2–10.0mm,
Rectangular: A> 0.8–8mm, B> 2-22.5mm
Square: 0.4*0.4mm–8*8mm
Foils:Thickness：0.2–2.5mm, width:60–1250mm

Copper Clad Aluminum Wire is a new enameled wire, is composed of aluminum conductor covered with copper materials, maybe self-bonding, also called self-bonding enameled wire. And the short word is ECCA.

The main advantages of fiberglass covered wire are:
1. The quality factor Q value is large;
2. Because it is twisted by multiple enameled wire bundles, it has good flexibility and can reduce the skin effect;
3. Because it is composed of polyurethane enameled wire, the dielectric loss angle is small, and it has direct solderability.
The disadvantage is: poor moisture resistance.

The wire drawing metal processing technology can form fine lines on the surface of the metal material, which makes the metal more textured, and is used as a decoration by users and is well-loved. In the production process, the drawing lubricating fluid is indispensable in the drawing metal processing technology. It is widely used in the lubrication of the middle drawing, small drawing and micro drawing of enameled copper wire. So how to choose this kind of drawing fluid?

Copper Clad Aluminum Enameled Wire is one of magnet wire, used for electric equipment. ECCA is popular enameled wire, maybe instead of the copper enameled wire and aluminum magnet wire in some field.

Three-layer insulated wire structure
High-frequency transformer triple-insulated wire is a high-performance insulated wire, so as the name suggests, this wire has three insulation layers with a core wire in the middle.
The first layer The first layer is golden yellow polyamine film, its thickness is a few microns, but it can withstand 3KV pulse high voltage
The second layer is a spray paint coating with high insulation,
The third layer is a transparent glass fiber layer. The total thickness of the insulating layer is only 20-100um. Its advantage is high insulation strength, and any two layers can withstand a safe voltage of 3000V AC, and the current density is large.

Anti-electricity-firecable wire
2. Aluminum winding wire
3. Three-layer extruded insulation wire

3.1 Elongation:
The standard refers to GB/T6109, inspection method: stretch the instrument
Calculation method: ratio of (length after stretching-length before stretching)/length before stretching;

3.2 Snap off:
The standard is to pull at a speed of 2 meters per second to check that the paint film is not cracked,

3.3 Round rod winding:
Wrap the enameled wires of different specifications and the corresponding copper rods around ten times to check that the paint film is not cracked. The diameter of the copper rods refers to the requirements of GB/T6109;

3.4 Thermal shock: Put the winding enameled wire in an oven (hanging in the middle of the oven) for 0.5 hours. The temperature of the oven corresponds to the specification requirements of the enameled wire. Refer to GB/T6109. After the drying, check that the paint film is not cracked.

Certification: SGS,UL
Size: 0.2mm-8.0mm
Delivery time: 10-30days
Thermal Class: 130-220C
Conductor Material: Copper Clad Aluminum

Correspondence table of enameled wire diameter and resistance value
The resistivity of the copper wire ρ= 0.0172, the aluminum wire ρ = 0.0283, the wire resistance calculation formula:
R=ρ×L/S
(L = wire length, unit: meter, S = wire cross section, unit: mm^2)

The current mainly passes along the copper-clad aluminum wire on the surface of the wire, which is called the skin effect. The higher the frequency, the more obvious it is. The copper-clad aluminum wire uses this feature to save material. But its resistivity is slightly higher than that of pure copper wire, and the resistivity is also different with the thickness of the copper clad.

Standards Of Enameled Wire includes
1）IEC 60317 for Europe
2）JIS C3202 for Asia
3）NEMA MW 1000C (inch) or NEMA MW 1000C metric (mm) for North America

Heat resistance refers to the properties of a substance that can maintain its excellent physical and mechanical properties under heated conditions. The highest use temperature of commonly used materials to characterize. There are different standards and test methods for different materials. Such as plastics are generally expressed by Martin heat-resistant temperature. The coating industry uses a blast constant temperature oven or a high temperature furnace. After it reaches the specified temperature and time, the surface condition of the paint film is inspected, tested, or other properties such as impact, bending, water immersion, salt spray test, etc., and then before and after Test data representation. All coatings used in higher temperature occasions must use heat resistance as an important technical indicator of the coating film

The main advantage of the TIW wires is relatively high electric strength of the insulation, with breakdown voltage min. 6kV. Obtaining such a high resistance was possible by the use of a reinforced, three-layer conductor insulation. Third external insulation made of polyamide gives excellent flexibility and high mechanical resistance of the wire. Normally, TIW wires are produced in thermal class B. Fully automated manufacturing process provides a central position of conductor and the same thickness of insulation at any point of the wire.

According to SMM survey data, the operating rate of enameled wire in September was 71.32%, down 8.28% year-on-year, down 1.82% month-on-month, and 1.65% lower than the expected 72.97%. Among them, the operating rate of large enterprises was 71.56%, down 0.69% from the previous month; medium-sized enterprises fell by 4.06% to 71.50%, and small enterprises fell by 0.55% to 60.83%.

Enameled Aluminum Wire connects Enameled Copper Wire with the short service life according to the test. The contact part of the enameled copper wire and the enameled aluminum wire will accelerate the oxidation of the aluminum wire.

How to Choose your Wire Manufacturers? You want to choose competitive wire manufactuer, should think about the
Factory certificate
Wire specifications
Copper or aluminum pure

The current enamel wire industry is relatively low due to the admission threshold, and therefore the production enterprises have more and more, and the market competition is constantly intensified, but in the high-end product field, there are not many companies that can enter, in the present, and future, The enamel wire business wants to achieve better development, and build brands and scale becomes more and more important.

Main Applications:
All kinds of household electric motors, vacuum cleaner motor, electric motor
All kinds of transformers, inductors, rectifiers
All kinds of fan motor
All kinds of high frequency electric appliance

AWG magnet wire is also called enamelled manganin wire which is composed of copper or aluminum conductor with insulation materials, such as PE, EI, UE, etc. The enameled wire have different performance according to chemical performance, heat resistance and others.

The Flat magnet wire size:
155 modified polyester enameled rectangle wire: a: 1.00-5.00;b: 2.00-16.00
180 polyester imied enameled rectangle wire: a: 1.00-5.00;b: 2.00-16.00
220 polyester imied enameled rectangle wire: a: 1.00-5.00;b: 2.00-16.00
200 polyester imeid/polyamide-imide enameled rectangle wire: a: 1.00-5.00;b: 2.00-16.00

The round enameled wire size
155 modified polyester enameled aluminum round wire: 0.25mm – 2mm
200 polyester imeid/polyamide-imide enameled round copper wire:0.016-7mm

Question: During our production process, we found that one axis of enameled wire is wound around the axial inductance. This axis of enameled wire and other axis of enameled wire are wound on the same magnetic core. The inductance of the enameled wire with this axis is relatively high. We made 1mH inductance, and the enameled wire of the other axis was only 960uH, and the problematic wire of this axis was 1.025mH, and the inductance test frequency was 796kHz. (1) The number of stitches is the same as the number of turns, excluding the slip ring. (2) The 1-meter straight resistance is a bit smaller than that of other shafts. I personally think that the enameled wire contains magnetic substances, but if it contains magnetic substances, the resistivity should be greater, and the DC resistance should be greater. So please help to solve the problem, or have encountered this kind of problem before, please analyze it, thank you in advance!

1. Conductor resistance ¡ª The resistance of a conductor is proportional to its length and inversely proportional to its cross-sectional area.
2. Conductivity¡ªBased on the resistance 1/58ohm (0.017241 ohm) of a standard soft copper wire with a length of 1m and a cross-sectional area of 1mm2 at 20¡æ, it is called 100% conductivity. The greater the resistance, the lower the conductivity, and the two are inversely proportional.
3. Bending resistance¡ªfix one end of the single wire, add weight to the other end to make it vertically downward, and then bend it back and forth 180 times until the wire breaks. The more bending times, the stronger the bending resistance.
4. Tensile breaking force¡ªthe maximum load weight or force applied to the specimen to break it during a tensile test.
5. Tensile strength¡ªthe breaking force per unit area to bear when the sample is broken during the tensile test.
6. Elongation ¡ª the ratio of the length of the sample after being stretched until it breaks to the original length at the specified standard distance. Conductors have different impedances at different temperatures.
Generally, 20¡ãC or 25¡ãC is the standard. The higher the temperature, the greater the impedance.

Enameled wire is coated with insulating paint on the outside of the bare Aluminium wire, constitute the inside due to the effect of insulating varnish, between the two adjacent wire can bear 200 v ac voltage Q general insulation flow line surface light, soft, can work under the condition of 130 ¡æ continuous.In addition, enameled wire bending also requires 10 times, paint should not fall off, in order to meet the winding when won’t appear the quality problem.

The structure of enameled wire is very simple, consisting of conductor and insulating layer. Because of its high dielectric strength, small footprint and good heat dissipation, it is widely used as a coil winding in motors and transformers.

The difference between enameled aluminum wire and enameled copper wire of vibration motor: the resistivity of copper wire is 0.017, and the resistivity of aluminum wire is 0.028. The cross-sectional ratio of copper wire and aluminum wire interchange is 0.79:1, and six square copper wires are equivalent to ten square aluminum wires. The diameter of the aluminum wire is thicker than that of the copper wire, and the same aluminum wire of the stator slot will not fit.

The wrapped wire is made of natural silk, polyester fiber, glass fiber, insulating paper or synthetic resin film, etc., tightly wrapped on the conductive wire core to form an insulating layer. There are also insulating layers wrapped around the enameled wire. In addition to thin-film insulation, others such as glass filaments need to be dipped in adhesive insulating varnish to improve their electrical, mechanical and moisture-proof properties. In fact, they are combined insulation.

The coating is a process of forming a uniform coating layer of a coating wire to form a uniform coating layer on a metal conductor. This is related to some physical phenomena and painting methods of liquid.