Paper wrapped insulated aluminium wire enamelled

The infrared spectrum analysis test is based on the standard UL746A, which only confirms the chemical composition of the paint film, establishes the infrared spectrum and retains it. After the enameled wire is certified, samples will be sampled for testing every year during the follow-up inspection service. The infrared spectrum made by the paint film on the sampled sample needs to be compared with the infrared spectrum established on the sample at the time of certification. The two infrared spectrums must be comparable. superior.

¡ñ Conductor resistance. Measure with a conductor resistance tester, and then change to the value at 20¡ãC for comparison.
¡ñInsulation destruction voltage. Twist two enameled wires, apply voltage between the conductors, and judge by the damage voltage of the paint film. This performance is analyzed and judged through two tests of normal state and cold state breakdown voltage.
¡ñPaint film continuity (pinhole). Check the small holes of the paint film with a certain length of the test material. The project is tested by a high-pressure paint film continuity tester.

A brief introduction to the advantages and disadvantages of copper wire and aluminum wire:Same area:

1, copper wireis large load than aluminum wire . 2, copper wire is more flexible than aluminum wire. 3 copper wire is lower resistivity than aluminum wire. 4,copper wire is more stable than aluminum wire. 5, however, copper wirer price is 3.5 times higher than aluminum wire.

List 5 type of enameled wire characteristics
Acetal enameled wire
Polyurethane enameled wire
Polyester and modified polyester enameled wire
Polyesterimide/polyamide imide composite enameled wire
Polyesterimide/polyamide composite enameled wire

Application:1. High-frequency transformers, ordinary transformers; 2. Inductances, electromagnetic coils; 3. Motors, including household motors, various micro motors, compressors and other motors with high environmental requirements; 4. Special electromagnetics for audio coils and optical drives Wire; 5. Electromagnetic wire for display deflection coil; 6. Electromagnetic wire for degaussing coil;

Three-layer insulated wire structure
High-frequency transformer triple-insulated wire is a high-performance insulated wire, so as the name suggests, this wire has three insulation layers with a core wire in the middle.
The first layer The first layer is golden yellow polyamine film, its thickness is a few microns, but it can withstand 3KV pulse high voltage
The second layer is a spray paint coating with high insulation,
The third layer is a transparent glass fiber layer. The total thickness of the insulating layer is only 20-100um. Its advantage is high insulation strength, and any two layers can withstand a safe voltage of 3000V AC, and the current density is large.

Polyimide Film Covered Aluminum Wire Production Process

One step :
Take the pure aluminum material drawing into the aluminium rod wire;
Two step :
Through the extrusion production line, take the aluminum rod wire into extruding and coarse drawing operation, then becoming the requirement specification of Bare aluminium wire;

Three step :
Take up the Bare aluminum wire conductor, and inspection the bare wire coil products;

Four step :
After annealing the alumium wire coil , cleaning and pay-off the wire coil, ready to next operation;

Five step :
Taking into straightening and Tension levelling operation, varnish treat the surface of wire, and then for the glass fiber covered;

Six step :
And then for baking the fiberglass wire , pulling the finished wire, and take-up the fiberglass wire products.

Product Introduction :
Nomex covering corresponds to class H insulation is mainly used in the construction of condensers and capacitors. Main application of it is in shielding of cables in high temp. environments (200¡ãC) such as dry type transformers, military and aerospace cables. Nomex covered conductors are more effective in condition where temperature resistance and dielectric strength requirements are high.

By extrusion of bare aluminum wire wrapped and Nomex Paper covered wire, the mechanical performance and electrical performance better, instead of making difficult composite enameled flat wire, suitable for transformer, winding of lifting electromagnet, electric welding machine and other products.

Use a hydrogen-oxygen flame welding machine to weld the coil lead wires of electronic devices such as motors, motors, and transformers.

working principle:
Water is composed of hydrogen and oxygen. In a specific electrolytic cell, water can be decomposed into hydrogen ions and hydroxide ions. The hydrogen ions move to the cathode to generate hydrogen gas, and the hydroxide ions move to the anode to generate oxygen. Hydrogen is a fuel. Oxygen can be used to support combustion. It can be ignited by a specific hydrogen-oxygen flame gun to form a hydrogen-oxygen flame, which can quickly weld the enameled wire.

Enameled wire production water also has many uses, and similarly, the requirements for water quality are also different. According to the water quality requirements of the purpose of use, it can be divided into: annealing furnace sealing water, equipment cooling water, lubricant manufacturing water, etc.

The structure of enameled wire is very simple, consisting of conductor and insulating layer. Because of its high dielectric strength, small footprint and good heat dissipation, it is widely used as a coil winding in motors and transformers.

Silver plated copper wire is manufacture with the combination of silver and copper and Silver Plated Copper Electrical Wire is manufactured using grade copper and silver; the industrial standards are always kept into the consideration.

Telephone cable is usually thought of only as a communication medium operating at a normal 48 Vdc level. But telephone cable is regularly used by telephone operating companies to supply power to remote telephony equipment such as: PCM (Pulse Code Modulation) repeaters, FDM (Frequency Division Modulation) repeaters, telegraph and various types of control circuits. The normal talk battery voltage is regularly exceeded in the case of long subscriber loops utilizing loop extenders and on dial long line circuits which operate in the 70 to 100 Vdc range. For these applications, the referenced devices are generally current limited to approximately 150 milliamps. In all such cases, normal telephone industry practice usually limits pair-toground applied voltage to 150 Vdc, and pair-to-pair voltage is usually limited to 300 Vdc.

Aluminum bare magnet wire (Anodized Bare Aluminium wire) belongs to the special electromagnetic wire and the insulation layer is the aluminum oxide .Because of no thermal aging phenomenon, it can be used as insulation level of class 220.
The insulation layer of such product is thin, high temperature resistance and insulation performance stability,which is the best choice for low voltage winding wires with producing high temperature, poor environment, heat dissipation difficulty and so on. It can widely be used in electromagnetic industries at home and abroad.

Copper-clad aluminum wire is made of a solid aluminum core covered with a copper skin in order to improve its performance in the field. Copper clad aluminum wire is very different from solid EC grade aluminum wire. For one, CCA belongs to a species of metals known as ¡°Bimetallics,¡±
Conductor materials: copper and aluminum

3.1 Elongation:
The standard refers to GB/T6109, inspection method: stretch the instrument
Calculation method: ratio of (length after stretching-length before stretching)/length before stretching;

3.2 Snap off:
The standard is to pull at a speed of 2 meters per second to check that the paint film is not cracked,

3.3 Round rod winding:
Wrap the enameled wires of different specifications and the corresponding copper rods around ten times to check that the paint film is not cracked. The diameter of the copper rods refers to the requirements of GB/T6109;

3.4 Thermal shock: Put the winding enameled wire in an oven (hanging in the middle of the oven) for 0.5 hours. The temperature of the oven corresponds to the specification requirements of the enameled wire. Refer to GB/T6109. After the drying, check that the paint film is not cracked.

The paper covered wire is a type of enameled wire that is extruded or pulled by an oxygen-free copper rod or an electrical circular aluminum rod, and then annealing the wire, and then winding two layers or two layers of insulating on the copper (aluminum) conductor.Paper (including telephone paper, cable paper, high voltage cable paper, turns], suitable for oil immersion transformer coils and other similar electrical windings.Electrical bare copper (aluminum) wires produced by extrusion process are the most ideal materials for the production of cable paper wraps.

FiberGlass covered Aluminum wire is according to customers requirement, aluminum conductor is evenly covered with one or two layers of non-alkali fiberglass, then it¡¯s impregnated in compatible insulating coating of required thermal class baked to make a whole between fiberglass and Aluminum conductor (optionally be applied to polyester and polyamide).

Generally speaking, UL certified enameled wire needs to do four tests:
Thermal Aging Test (Full Thermal Aging Test or One Temperature Thermal Aging Test)
Dielectric Strength Test
Elongation and Heat Shock Test
Infrared Analysis – IR

To weld the lead aluminum enameled wire, it is necessary to remove the paint (there are very few household electric fans with very low requirements, and the ballast manufacturer does not remove the paint). The paint removal methods are listed below.
(1) It can be scraped with a blade,
(2) It can be peeled with a centrifugal knife,
(3) The paint can also be rubbed off with a grinding wheel,
(4) Of course paint remover is also available,
(5) You can also use high-temperature tin to burn the paint,
(6) Some people burn with fire
(7) Of course you can also use paint remover to remove paint

Transformer oil: It is a fractionation product of petroleum, and its main components are alkanes, cycloalkane saturated hydrocarbons, aromatic unsaturated hydrocarbons and other compounds. Commonly known as square shed oil, it is a light yellow transparent liquid with a relative density of 0.895. Freezing point <-45¡æ.
Transformer oil is a kind of mineral oil obtained by distillation and refining from natural petroleum. It is a liquid natural hydrocarbon that is pure and stable, with low viscosity, good insulation, and good cooling by acid-base refining treatment of the lubricating oil fraction in petroleum. Mixture of compounds. Commonly known as square shed oil, light yellow transparent liquid.

ISO Certificated Polyimide Round Enamel Coated Magnet Wire has better performance than all other types of enameled wires. Polyimide paint film has only abrasion resistance slightly worse than polyester and polyvinyl acetal enameled wires. In order to improve this performance, most of the current Use polyester imide and polyamide imide to prepare enameled wire, which can increase the solid content of the paint, but the heat resistance is somewhat reduced.

ENAMELED ROUND ALUMINUM WINDING WIRES are widely used for Oil-immersed transformer windings, Dry-type transformer, High temperature transformer, Motor, transformer, generator, welding machine; Sealed motor, Power tools motor, Auto alternators motor, Magnet coil, High power motor, household electro motors and micro-motors;

7 type of enameled wire in accordance with insulation materials, list the thermal class, advatanges and application per type of enameled wire. Enameled wire types also can be divided into copper magnet wire and aluminum wire in accordance with conductor.

According to SMM survey data, the operating rate of enameled wire in September was 71.32%, down 8.28% year-on-year, down 1.82% month-on-month, and 1.65% lower than the expected 72.97%. Among them, the operating rate of large enterprises was 71.56%, down 0.69% from the previous month; medium-sized enterprises fell by 4.06% to 71.50%, and small enterprises fell by 0.55% to 60.83%.

Enameled wire is widely used in our production and life. The paint it uses is a kind of paint that can produce a good insulating layer between the wires in the winding.
Enameled wire is made on the basis of copper wire. Simply put, enameled wire is a layer of insulator on the copper wire, usually plastic. Enameled wire paint is a kind of outer layer of bare copper wire, alloy wire and glass wire covered wire of various wire diameters to improve and stabilize the performance of enameled wire. It has high mechanical strength, resistance to Freon refrigerant, good compatibility with impregnating paint, and can meet the requirements of heat resistance, impact resistance, oil resistance, etc.

After the product is manufactured, whether its appearance, size and performance meet the requirements of the technical standards of the product and the technical agreement of the user must be judged by the inspection beam and measured; the test shall be compared with the technical standard of the product or the technical agreement of the user and meet the requirements If it is qualified, otherwise, it is unqualified. Passing the inspection can reflect the stability of the enameled wire product quality, the material and the rationality of the process. Therefore, the quality inspection has the function of checking, preventing and identifying.

Carbon aluminum wire is an aluminum wire for parts manufacturing of various machines.08 and 08F aluminum wire for rolling thin plates, deep-drawing products, oil drums, high-grade enamel products, less demanding carburizing and cyanide parts, welding rods, etc.

Inductive sensors have outstanding advantages such as simple structure, fast dynamic response, and easy non-contact measurement. They are especially suitable for acids, alkalis, chlorides, organic solvents, liquid CO2, ammonia, PVC powder, ash, oil and water. Liquid level measurement such as interface is currently widely used in metallurgy, petroleum, chemical, coal, cement, food and other industries.

The space factors of magnet wires are compared in the right figure. The space factors of enamelled wires are superior to those of other wires for winding, as are their electrical properties. However, more careful examination must be made of the following properties as compared with other wires.