Enameled wire welding paint removal

The infrared spectrum analysis test is based on the standard UL746A, which only confirms the chemical composition of the paint film, establishes the infrared spectrum and retains it. After the enameled wire is certified, samples will be sampled for testing every year during the follow-up inspection service. The infrared spectrum made by the paint film on the sampled sample needs to be compared with the infrared spectrum established on the sample at the time of certification. The two infrared spectrums must be comparable. superior.

To weld the lead aluminum enameled wire, it is necessary to remove the paint (there are very few household electric fans with very low requirements, and the ballast manufacturer does not remove the paint). The paint removal methods are listed below.
(1) It can be scraped with a blade,
(2) It can be peeled with a centrifugal knife,
(3) The paint can also be rubbed off with a grinding wheel,
(4) Of course paint remover is also available,
(5) You can also use high-temperature tin to burn the paint,
(6) Some people burn with fire
(7) Of course you can also use paint remover to remove paint

1. Cutting
The enameled wire is composed of a conductor and an insulator, and the hardness of the two parts is very soft, so it can be cut by using a TabCUT-200 precision cutting machine with a general SiC cutting chip. Since the insulator is coated on the conductor, and its hardness and ductility are quite different, and the insulating layer has a certain degree of peeling, it is better to use some soft materials such as tin foil, rubber, etc. to wrap the cutting part when cutting. Up to prevent the insulation layer at the fracture from peeling off after cutting.

The temperature resistance index of Class 155 Reasonable Price Glass Fiber Covered Aluminum Round Wire has three grades: 130, 155, and 180, and the insulation thickness generally has four grades of 20, 30, 40, and 50. This product is widely used in windings of transformers, electromagnets, welding machines or other similar electrical equipment products. Electrician bare aluminum wire produced by extrusion process is the most ideal material for producing glass fiber coated aluminum wire.

Enameled wire is a main type of winding wire. It is made of a metal conductor as a conductive inner core and coated with a polymer insulating layer. It is mainly composed of these two parts; it is the conversion of electromagnetic energy into mechanical energy, heat energy, sound energy, light energy or machinery Functional materials that convert energies such as heat, heat, chemistry, sound and light into electromagnetic energy.

The temperature resistance of composite enameled wire can reach above 520 degrees.
Composite enameled wire is an ideal wrapping wire for large-scale low-voltage and high-current electrical appliances such as power oil-immersed, dry-type, special transformers, electric welding machines, reactor rectifiers, electromagnetic separators, etc., with excellent electrical performance and stability.

The heat resistance class of enameled wire is the ambient temperature where the enameled wire can work normally for a long time (above 20000h).

Good Quality Paper Covered Flat Aluminum Enameled Copper Wire is made of bare copper wire or bare aluminum wire, or paper-covered wire as the core, wrapped with paper for insulation. According to customer and national standards, the conductor is wrapped with telephone paper, electromagnetic paper, and high-density inter-turn insulation paper. As conductor insulation, it is an ideal material for civilian-made oil-immersed transformers; especially semi-hard insulated copper wires, which can significantly improve the winding resistance. The mechanical properties and short-circuit resistance can be widely used in the winding of large and medium-sized transformers.

British Standard Wire Gauge (often abbreviated to Standard Wire Gauge or SWG) is a unit for denoting wire size given by BS 3737:1964 (now withdrawn). It is also known as the Imperial Wire Gauge or British Standard Gauge. Use of SWG sizes has fallen greatly in popularity, but they are still used as a measure of thickness in guitar strings and some electrical wire. Cross sectional area in square millimetres is now the more usual size measurement for wires used in electrical installation cables. The current British Standard for metallic materials such as wire and sheet is BS 6722:1986, which is a solely metric standard.

Nomex covering corresponds to class H insulation is mainly used in the construction of condensers and capacitors. Main application of it is in shielding of cables in high temp. environments (200¡ãC) such as dry type transformers, military and aerospace cables. Nomex covered conductors are more effective in condition where temperature resistance and dielectric strength requirements are high.
Application of Nomex Paper Covered Aluminum wire :
Mobile Transformer,Traction Transfomers,Pole-mounted distribution transformers,Power substantions,rectifiers,oil-immersed transfomer coil winding.

Principle: Water molecule (HHO) decomposes water into oxygen and hydrogen through electrolysis. Hydrogen is combustible. Oxygen supports combustion. These two gases are ignited to form a hydrogen-oxygen flame. In layman’s terms, “water turns into fire”

ENAMELED ROUND ALUMINUM WINDING WIRES are widely used for Oil-immersed transformer windings, Dry-type transformer, High temperature transformer, Motor, transformer, generator, welding machine; Sealed motor, Power tools motor, Auto alternators motor, Magnet coil, High power motor, household electro motors and micro-motors;

The enamel wire is a major variety of winding wires, composed of two conductors and insulating layers, after the naked wire is deck, and then painted, baked.However, it is not easy to produce products that meet the standard requirements, but also meet customer requirements, it is affected by factors such as raw materials, process parameters, production equipment, environment, and therefore, the quality characteristics of various enameled wires are different, but they haveFour major properties of mechanical properties, chemical properties, electrical properties, and thermal performance.

Polyimide Film Covered Aluminum Wire Production Process

One step :
Take the pure aluminum material drawing into the aluminium rod wire;
Two step :
Through the extrusion production line, take the aluminum rod wire into extruding and coarse drawing operation, then becoming the requirement specification of Bare aluminium wire;

Three step :
Take up the Bare aluminum wire conductor, and inspection the bare wire coil products;

Four step :
After annealing the alumium wire coil , cleaning and pay-off the wire coil, ready to next operation;

Five step :
Taking into straightening and Tension levelling operation, varnish treat the surface of wire, and then for the glass fiber covered;

Six step :
And then for baking the fiberglass wire , pulling the finished wire, and take-up the fiberglass wire products.

Kapton insulated aluminium wires are suitable for both HV and UHV applications at temperatures ranging from -269 to 200¡ãC with maximum bakeout temperature of 260¡ãC.
Kapton insulated aluminum wire is designed for use in high & ultra-high vacuum applications. Kapton has high mechanical strength, excellent electrical insulation properties, and low outgassing rates making it ideal for use as an in-vacuum insulator. These wires can be utilized in temperature ranges from 4K to 260¡ãC.

Water quality affects the production of lacquer wires?

The production water production water in the lacquered wire has a variety of uses, and like, the requirements for water quality are also different. Depending on the purpose of use, the water quality can be divided into: annealing furnace water seal water, equipment cooling water, lubricant manufacturing water, etc.

Certification: SGS,UL
Size: 0.2mm-8.0mm
Delivery time: 10-30days
Thermal Class: 130-220C
Conductor Material: Copper Clad Aluminum

Enameled round aluminum wire is made of oxygen free rod or electrical aluminum rod by a certain size of the die drawing or extrusion of the wire, the insulation paint through many times of the winding wire. Mainly used in winding of transformers, motors, generators, and various electrical devices.

The environmental painted wires of the lacquer formula contains the shortening project development time, saving project funding, and significantly improving the quality of the project.

What is the first thing to make the enamel wire? And the manufacutring process of enameled wire is important, the extruding and baking. And the raw materials: copper conductor or aluminum conductor is enough for client’s requiremnets

The multi-shaped enamel wire refers to a metal wire for winding electromagnetic coils with an insulating paint, also known as electromagnetic wires. The multi-shaped enameled wire is the primary raw material of electrical, motor and household appliances, telecommunications, electronic external electromagnetic windings. In the future, follow the rapid development of industrial appliances, household appliances, telecommunications, electronic products, etc. Market and application fields.

Another important usage of copper is in manufacturing wire gauges that are largely use in measuring the diameter of wire.
Similarly aluminium is also largely use for electrical application.

1. Conductor resistance ¡ª The resistance of a conductor is proportional to its length and inversely proportional to its cross-sectional area.
2. Conductivity¡ªBased on the resistance 1/58ohm (0.017241 ohm) of a standard soft copper wire with a length of 1m and a cross-sectional area of 1mm2 at 20¡æ, it is called 100% conductivity. The greater the resistance, the lower the conductivity, and the two are inversely proportional.
3. Bending resistance¡ªfix one end of the single wire, add weight to the other end to make it vertically downward, and then bend it back and forth 180 times until the wire breaks. The more bending times, the stronger the bending resistance.
4. Tensile breaking force¡ªthe maximum load weight or force applied to the specimen to break it during a tensile test.
5. Tensile strength¡ªthe breaking force per unit area to bear when the sample is broken during the tensile test.
6. Elongation ¡ª the ratio of the length of the sample after being stretched until it breaks to the original length at the specified standard distance. Conductors have different impedances at different temperatures.
Generally, 20¡ãC or 25¡ãC is the standard. The higher the temperature, the greater the impedance.

The selection criterion of the electromagnetic wire is not considered for resistance, as the problem of resistance and fever can be done by selecting the same cross-sectional wire, it is the main consideration of the thick wire or the thin wire is mainly considered Operability.

Copper-clad aluminum wire refers to a wire with aluminum core wire as the main body and a certain proportion of copper layer plated on the outside. It can be used as a conductor for coaxial cables and wire and cable conductors in electrical equipment. The aluminum wire has a small specific gravity, but its welding performance is not good. Therefore, the copper-clad aluminum wire is wrapped with a copper layer on the aluminum wire. This copper-clad aluminum wire can not only take advantage of the small aluminum specific gravity, but also improve the welding performance.

1. Mechanical function: including elongation, return angle, softness and adhesion, scraping, tensile strength and other items.
2. Heat resistance: including thermal shock and softening breakdown test.
3. Electricity includes: breakdown voltage, lacquer film continuity and DC resistance test.
4. Chemical resistance includes solvent resistance and welding.

Speaking of the copper enameled wire, I believe everyone should know. Today, we introduce you to a wire, ie the copper paint package. Let us simply look at the transportation and preservation of copper-clad aluminum wires, because if many wires are transported incorrect, it is very likely to be used, so let us simply understand the transportation and preservation of the copper paint wire, so you can be here.

Class F Glass Fibre Insulated Aluminium strips is a high-quality aluminum wire that is evenly wrapped with alkali-free glass fiber. It is impregnated and baked with the required temperature resistance index and compatible bonding paint to make the glass fiber between the glass fiber It is bonded to the conductor as a whole, and the insulating layer has a certain degree of wear resistance, adhesion, flexibility and voltage resistance. This type of winding wire has good thermal shock and overload resistance. At present, the temperature resistance index of this kind of products has three grades: 130, 155, and 180. F grade refers to 155 grade.

After the temperature resistance level is exceeded, the insulation layer will age, melt and crack. The result is that the insulation capacity is greatly reduced, and it is prone to increased loss, short-circuit failure, etc.