High Performance Coil Magnet Aluminum winding wire

A brief introduction to the advantages and disadvantages of copper wire and aluminum wire:Same area:

1, copper wireis large load than aluminum wire . 2, copper wire is more flexible than aluminum wire. 3 copper wire is lower resistivity than aluminum wire. 4,copper wire is more stable than aluminum wire. 5, however, copper wirer price is 3.5 times higher than aluminum wire.

Enameled Aluminum Wire Compared To Enameled Copper Wire have some advantages
Aluminum /Copper Wire/foils
Dimension:0.2–10.0mm,
Rectangular: A> 0.8–8mm, B> 2-22.5mm
Square: 0.4*0.4mm–8*8mm
Foils:Thickness：0.2–2.5mm, width:60–1250mm

The AWG tables are for a single, solid and round conductor. The AWG of a stranded wire is determined by the cross-sectional area of the equivalent solid conductor. Because there are also small gaps between the strands, a stranded wire will always have a slightly larger overall diameter than a solid wire with the same AWG.

Enameled wire production water also has many uses, and similarly, the requirements for water quality are also different. According to the water quality requirements of the purpose of use, it can be divided into: annealing furnace sealing water, equipment cooling water, lubricant manufacturing water, etc.

Copper-clad aluminum wire is made of a solid aluminum core covered with a copper skin in order to improve its performance in the field. Copper clad aluminum wire is very different from solid EC grade aluminum wire. For one, CCA belongs to a species of metals known as ¡°Bimetallics,¡±
Conductor materials: copper and aluminum

Application of enamel coated magnet wire
Wire for winding used in electrical equipment is generally called magnet wire. Simplyput,”enamel coated magnet wire is used for interchanging electrical energy with magnetic energy”.Magnet wires are broadly divided into enamelled wire (coating insulation), coveredconductor wire (fiber/film insulation), and combinations thereof.

In recent years, the price of electrolytic copper has continued to rise, which has brought a huge impact to the production of related copper wire raw materials and enameled wire suppliers. The use of copper-clad aluminum enameled wire has been proved by users to replace pure copper enameled wire, thus providing a huge business opportunity and a broad market for the development of my country’s enameled wire industry. The new type of Enameled Copper Coated Aluminum Magnet Wire For Voice Winding using copper clad aluminum material as the inner conductor has characteristics between copper and aluminum, combining the excellent conductivity of copper and the light weight of aluminum.

Winding wires used in electrical equipment are usually called magnetic wires. In other words, “magnetic wires are used to exchange electrical energy and magnetic energy.” Magnetic wire is roughly divided into enameled wire (insulation coated) and coated wire (fiber/film insulation) and their combinations. The two types of magnetic wires and their performance are very different. ASTM (American Society for Testing and Materials) B193, no more than 0.017241 ohm (square millimeter/meter), the film or coating should meet the latest version of ANSI, ASTM or NEMA applicable standards, and modify the specified resin. The modified resin is Chemically changed resin, or containing one or more additives to retain the basic chemical characteristics of the original resin to enhance certain performance or application characteristics, the coated conductor needs to meet all the required test requirements of the appropriate NEMA standard (UL certification project) .

Best Selling 155 Class Enamelled Copper/Aluminum Winding Wire includes copper wire and aluminum wire used for transformers, inductors, motors, generators, dry type transformer, Cast Resin Transformers. Thermal Class:Class 155, popular used for low voltage dry type transformers.

Class F Glass Fibre Insulated Aluminium strips is a high-quality aluminum wire that is evenly wrapped with alkali-free glass fiber. It is impregnated and baked with the required temperature resistance index and compatible bonding paint to make the glass fiber between the glass fiber It is bonded to the conductor as a whole, and the insulating layer has a certain degree of wear resistance, adhesion, flexibility and voltage resistance. This type of winding wire has good thermal shock and overload resistance. At present, the temperature resistance index of this kind of products has three grades: 130, 155, and 180. F grade refers to 155 grade.

Painted wire (electromagnetic wire) is the base and key material of the motor, electrical, household appliance, electronics, instrumentation, electromagnetic windings. With the rapid development of my country’s home appliance industry, electronic information, automobile and other industries, the scale of electromagnetic wire production enterprises expanded, and the country has developed from thousands of tons to the 10,000-tonnes. The rapid development of industrial appliances, household appliances, automotive and other industries, bringing electromagnetic wires and markets, but at the same time, rapid advancement of technology has made a growing demand for electromagnetic wires.

In the long-term thermal aging test, three or more temperature points are usually selected for accelerated aging, commonly known as “three-point aging”.

The samples for the aging test are stranded enameled wire pairs. The production of the stranded pairs should meet the requirements of ASTM D2307 or NEMA 1000 standards, including the weight to be applied when making the stranded pairs, the number of twisted turns, the effective length of the stranded area, and The length of the two ends of the twisted pair, etc. When making a twisted pair, the required force and the number of twist turns will vary depending on the diameter of the wire. The effective length of the stranded area has nothing to do with the wire diameter, the effective length is 121¡À6 mm, and the two ends are at least 50 mm long. At least 10 twisted pairs per temperature point and mounted on twisted pair racks for high temperature aging test.

Copper Magnet Wire Manufacturing Process includes important three steps – enameling, winding and Inorganic insulated wires. Mainly introduce the method to ensure the quality of copper enameled wire.

Enameled wire is used for camcorder, electronic clock, micro relay, automobile, electronic instrument, washing machine, TV element, etc. Development direction in the diameter, use the specification range of ¦Õ0.06 ~ 0.08 mm and all thickened insulation

The electrical insulation system for wires used in generators, electric motors, transformers, and other wire-wound electrical components is divided into different classes by temperature and temperature rise. The electrical insulation system is sometimes referred to as insulation class or thermal classification. The different classes are defined by NEMA, Underwriters Laboratories (UL), and IEC standards.

Polyimide Film Covered Aluminum Wire Production Process

One step :
Take the pure aluminum material drawing into the aluminium rod wire;
Two step :
Through the extrusion production line, take the aluminum rod wire into extruding and coarse drawing operation, then becoming the requirement specification of Bare aluminium wire;

Three step :
Take up the Bare aluminum wire conductor, and inspection the bare wire coil products;

Four step :
After annealing the alumium wire coil , cleaning and pay-off the wire coil, ready to next operation;

Five step :
Taking into straightening and Tension levelling operation, varnish treat the surface of wire, and then for the glass fiber covered;

Six step :
And then for baking the fiberglass wire , pulling the finished wire, and take-up the fiberglass wire products.

Insulation, also called insulating coatings, is a kind of coating with excellent electrical insulation. It has good electrochemical properties, thermal properties, mechanical properties and chemical properties, mostly varnishes, but also colored paints. Insulating paint is a special paint in the paint category. Insulating varnish is an important insulating material based on high molecular polymers that can be cured into an insulating film or insulation under certain conditions. Insulating paint is composed of base material, flame retardant, curing agent, pigment and filler, and solvent. It introduces its composition, usage classification, grade classification, requirements, development trend, etc. in detail.

Main Applications:
All kinds of household electric motors, vacuum cleaner motor, electric motor
All kinds of transformers, inductors, rectifiers
All kinds of fan motor
All kinds of high frequency electric appliance

The difference between enameled aluminum wire and enameled copper wire of vibration motor: the resistivity of copper wire is 0.017, and the resistivity of aluminum wire is 0.028. The cross-sectional ratio of copper wire and aluminum wire interchange is 0.79:1, and six square copper wires are equivalent to ten square aluminum wires. The diameter of the aluminum wire is thicker than that of the copper wire, and the same aluminum wire of the stator slot will not fit.

ISO Certificated Polyimide Round Enamel Coated Magnet Wire has better performance than all other types of enameled wires. Polyimide paint film has only abrasion resistance slightly worse than polyester and polyvinyl acetal enameled wires. In order to improve this performance, most of the current Use polyester imide and polyamide imide to prepare enameled wire, which can increase the solid content of the paint, but the heat resistance is somewhat reduced.

The wire drawing metal processing technology can form fine lines on the surface of the metal material, which makes the metal more textured, and is used as a decoration by users and is well-loved. In the production process, the drawing lubricating fluid is indispensable in the drawing metal processing technology. It is widely used in the lubrication of the middle drawing, small drawing and micro drawing of enameled copper wire. So how to choose this kind of drawing fluid?

Use a hydrogen-oxygen flame welding machine to weld the coil lead wires of electronic devices such as motors, motors, and transformers.

working principle:
Water is composed of hydrogen and oxygen. In a specific electrolytic cell, water can be decomposed into hydrogen ions and hydroxide ions. The hydrogen ions move to the cathode to generate hydrogen gas, and the hydroxide ions move to the anode to generate oxygen. Hydrogen is a fuel. Oxygen can be used to support combustion. It can be ignited by a specific hydrogen-oxygen flame gun to form a hydrogen-oxygen flame, which can quickly weld the enameled wire.

Water quality affects the production of lacquer wires?

The production water production water in the lacquered wire has a variety of uses, and like, the requirements for water quality are also different. Depending on the purpose of use, the water quality can be divided into: annealing furnace water seal water, equipment cooling water, lubricant manufacturing water, etc.

The samples for tensile and thermal shock testing were 3 pieces of 254mm enameled wire.

First pull the enameled wire to the required elongation at a rate of 3.7-4.6 m/sec, then wrap the jerked sample around the mandrel, and then put the wrapped sample into the oven at the specified temperature for 30 minutes. It needs to be suspended in the oven. After leaving the oven, inspect the baked samples for cracking or peeling of the paint film. In this test, the diameter of the mandrel is usually 3 times the diameter of the enameled wire.

The specified temperature of the oven is set according to the temperature specified for the enameled wire of this ANSI Type in the NEMA MW1000 standard, which is usually the temperature grade of the enameled wire +20¡ãC.

The main advantage of the TIW wires is relatively high electric strength of the insulation, with breakdown voltage min. 6kV. Obtaining such a high resistance was possible by the use of a reinforced, three-layer conductor insulation. Third external insulation made of polyamide gives excellent flexibility and high mechanical resistance of the wire. Normally, TIW wires are produced in thermal class B. Fully automated manufacturing process provides a central position of conductor and the same thickness of insulation at any point of the wire.

The infrared spectrum analysis test is based on the standard UL746A, which only confirms the chemical composition of the paint film, establishes the infrared spectrum and retains it. After the enameled wire is certified, samples will be sampled for testing every year during the follow-up inspection service. The infrared spectrum made by the paint film on the sampled sample needs to be compared with the infrared spectrum established on the sample at the time of certification. The two infrared spectrums must be comparable. superior.

Nomex covering corresponds to class H insulation is mainly used in the construction of condensers and capacitors. Main application of it is in shielding of cables in high temp. environments (200¡ãC) such as dry type transformers, military and aerospace cables. Nomex covered conductors are more effective in condition where temperature resistance and dielectric strength requirements are high.
Application of Nomex Paper Covered Aluminum wire :
Mobile Transformer,Traction Transfomers,Pole-mounted distribution transformers,Power substantions,rectifiers,oil-immersed transfomer coil winding.

Poor soldering is mainly manifested in that the paint film after soldering will not melt off after the soldering, which causes the phenomenon of poor soldering.

The main advantages of fiberglass covered wire are:
1. The quality factor Q value is large;
2. Because it is twisted by multiple enameled wire bundles, it has good flexibility and can reduce the skin effect;
3. Because it is composed of polyurethane enameled wire, the dielectric loss angle is small, and it has direct solderability.
The disadvantage is: poor moisture resistance.

Enameled Aluminum Wire connects Enameled Copper Wire with the short service life according to the test. The contact part of the enameled copper wire and the enameled aluminum wire will accelerate the oxidation of the aluminum wire.